Excimer laser irradiation induced formation of diamond-like carbon layer on graphite

摘要

Highly oriented pyrolytic graphite (HOPG) was irradiated by an ArF excimer (#lambda#=193 nm) laser above the ablation threshold, at approx. 0.45 and 2 J/cm~2. The surface morphology and the quality of the remaining material was investigated by atomic force microscopy (AFM) and area-selective Raman spectroscopy. At the lower fluence a material removal rate of several monolayers per laser pulse was detected, without changing the quality of the remaining material. Irradiation at the higher fluence resulted in ablation rates of the order of 10 nm/pulse and the formation of an approx. 300 nm thick diamond-like carbon (DLC) film with approx. 50