Evaluation of Polymeric Coatings in CO_2 Containing Environment

摘要

Two types of polymeric coating were applied on an AISI 1020 steel, where one of them was reinforced by carbon nanotubes, with the objective of protection against corrosion in a medium containing saline solution, NaCl 3% wt satured with CO_2, at 75 bar and tested at 50°C and 75°C for 360 hours. Electrochemical techniques, such as Linear Polarization Resistance, (LPR), Electrochemical Impedance Spectroscopy (EIS), Tafel curves and weight loss method, were used for coating evaluation performance. Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) wereused to determine both the morphology and chemical composition of the layer formed on the analyzed surfaces. The coating adhesion to metallic surface was evaluated using pull-off test according to ASTM D4541-09. For the studied conditions, the results obtained showed that there was no adequate coating protection, occurring failures and indicating that both coatings may not be used in the tested conditions.