Studies on incorporation of exfoliated bentonitic clays in polyurethane foams for increasing flame retardancy

摘要

In this contribution we report the results of studying the incorporation of exfoliated bentonitic clays into polyurethane foams. A suspension in water of a sodium bentonite from Argentine Patagonia was interchanged with cetyl trimethyl ammonium bromide (CTAB) for 4 h at 80°C, rendering an exfoliated clay, which is nanometric in only one dimension. This nanoclay, when dispersed in the polyurethane, resulted in the same fire retardancy rating (UL-94) than when polyurethane was treated with a commercial nanoclay. Scanning electron microscopy (SEM) at low augmentations of polyurethane samples treated with the synthethized nanoclay (2,5% w/w) showed no differences respect to untreated polyurethane, except for the irregularity of void edges.