Effect of Cold Rolling Treatment on the Formation of Titanium Oxide Layer on Ti6AI4V Alloys by Thermal-electrochemical Anodizing Processes

摘要

The present work concerns on preparing suitable titanium alloy substrate that might induce better characteristic of titanium oxide layer on the substrate. Different degrees of cold rolling treatments were applied on Ti6A14V alloy before thermal-electrochemical anodizing processes. The later processes were performed to produce titanium oxide layer which combines thermal process by heat treatment and followed with electrochemical anodizing process. After thermal heat treatment process, it was observed more homogeneous titanium oxide layer for the samples given cold rolling treatment as compared with sample without the treatment. This condition is believed due to the finer substrate surface after cold rolling treatment as observed from surface roughness measurement. Similar situation was observed after anodizing process that irregular oxidized layer was observed for sample without cold rolling treatment, whereas more homogenous layer was observed for sample with cold rolling treatment. Except for sample without cold rolling treatment, anodizing treatment tends to create finer oxidized layer. Therefore, it can be concluded that cold rolling treatment on titanium substrate before oxidizing process induces the formation of homogeneous oxide layer, whereas additional anodizing process create finer titanium oxide layer.