Photoelectrocatalytic Properties of Porous TiO_2 Films Prepared Using ODA as Template

摘要

The functions of applied potential to the photoelectrocatalytic degradation process of methyl orange were investigated. When using 0.05 M NaCl and under different applied potentials, the degradation rate increased obviously with increasing applied potential. When the applied potential was between 0.6 V-1.0 V, the degradation rate was enhanced drastically. The detected current values got larger as the applied potential increased from 0 up to 1.2 V. There was no direct electro-degradation to the dye in the solution. The applied potential and the irradiated light had synergetic effect when they were applied to the solution at the same time. While after irradiation for 0 to 60 min, with the increasing reaction time, methyl orange absorption peak intensity shrank obviously. The azo and benzene groups in methyl orange degraded totally under photocatalytic process.