Study on Characterization of Cationic Polyelectrolyte Modified Benzoguanamine Formaldehyde/Silica Composite Abrasives Slurry

摘要

In this paper, the adsorption characteristics of cationic polyelectrolyte PDADMAC on BGF particles and the Zeta potential of BGF particles have been investigated. A new type of composite abrasives slurry was obtained with cationic polyelectrolyte modified BGF particles and its polishing performance was studied. Experimental results showed that the Zeta potential of the modified BGF particles was changed from negative to positive and the maximum value (+35mv) was obtained when the adsorption saturation was achieved, and the adsorption capacity of SiO_2 abrasives on BGF particles was improved significantly. The material removal rate was 469nm/min with the modified BGF/SiO_2 composite abrasives slurry containing 5% SiO_2 and 3% modified BGF particles, increasing by 47% and 89% than those of the unmodified BGF/SiO_2 composite abrasives slurry (319nm/min) and the single silica abrasives slurry (248nm/min), respectively.