Mechanical Properties of PDMS/CNTs Nanocomposites

摘要

This study presents the mechanical and electrical properties (including elastic modulus, yield strength and electrical resistance) of PDMS/CNTs nanocomposites. The elastic modulus of pure PDMS and PDMS/CNTs nanocomposites were determined from tensile tests. In addition, a high resistance meter was used to measure the electrical resistances of the PDMS/CNTs nanocomposites. The test specimens of nanocomposites were manufactured using the thermoforming method. There were two recipes used during the thermoforming process: 100°C for 1 hour, and 150°C for 15 minutes. The mixtures of PDMS and CNTs were stirred by ultrasonic instrument to prevent polymerization. A feeler gap was used to define the thickness of the specimens. Therefore, the thickness could be controlled within the range of ～100□m. Four different kinds of specimens were investigated, including pure PDMS, 1.0 wt%, 2.0 wt% and 4.0 wt% CNTs polymeric composites. As for the 100°C recipe, the elastic modulus of pure PDMS, 1.0 wt%, 2.0 wt%, and 4.0 wt% CNTs were 1.05MPa, 1.17MPa, 1.10MPa and 1.35MPa, respectively. A for the 150°C recipe, the elastic modulus of pure PDMS, 1.0 wt%, 2.0 wt% and 4.0 wt% CNTs were 1.32MPa, 1.42MPa, 1.43MPa, and 1.54MPa. The differences of electrical resistance of PDMS/CNTs nanocomposites at two different conditions and the microstructures composed of the mixtures are also described in this article. 004PDMS/CNTs (polydimethylsiloxane and carbon nanotubes)