A Study of the Failure Wave Phenomenon in Glasses at Peak Stresses Exceeding the HEL

摘要

Shock-wave experiments with two glasses of different hardness have been carried out at shock stress levels above the Hugoniot elastic limit. A comparison between the measured free surface velocity histories from two plate impact experiments performed at approximately the same shock stress level (one with a single thick target plate, and the other with several adjacent target plates of total thickness equal to that of the thick target plate) revealed: 1) at shock loading the failure wave is not formed at stress levels above the HEL, indicating suppression of the fracture process by plasticity, 2) at gradual compression the failure wave process occurs as the stress increases above the failure threshold up to the stress at which plastic deformation begins.