Structure and mechanical properties of age-hardened directionally solidified AlSiCu alloys

摘要

The structure of directionally solidified Al-Si hypoeutectic alloys are generally composed of Al-matrix and Si-reinforcing phase. The growth direction of the both phases was near <200>. The strength properties of an Al-Si alloy with additions of 2 wt.% and 4 wt.% copper have been investigated. These alloys were solution treated, quenched in water and aged at 200°C. Large Al{sub}2Cu precipitates present in D.S. samples dissolved partly, and after ageing, they precipitated as theθ' platelets,significantly increasing the mechanical properties of the alloys. Hardness, strength and elongation were measured in the course of ageing. The structure was investigated by means of: XSAS, X-ray phase analysis, lattice parameter measurements and scanningmicroscopy.