Effect of storage and ball milling on the sedimentation and rheology of a novel magnetorheological fluid

摘要

In this study, the sedimentation stability and rheology of a new magnetorheological fluid formulation were experimentally investigated before and after being stored for 24 months, as well as after being milled. The results reveal that, after undergoing 24 months of steady storage, the off-state viscosity and field-induced yield stress of the MR fluid remained constant, and that its flowability and redispersibility were maintained. After being subjected to ball milling for 2 hours at 200 rpm and 300 rpm, the field-induced yield stress was also maintained.