Water Diffusion in Methacrylate Based Copolymer Hydrogels of 2-Hydroxyethyl Methacrylate

摘要

The diffusion of water into cylinders of polyHEMA and copolymers of HEMA with THFMA, BMA and CHMA were studied over a range of copolymer compositions. The diffusion of water into the polymers was found to follow a Fickian, or case I mechanism. The diffusion coefficients of water were determined from mass measurements and NMR imaging studies. They were found to vary from 1.7 ± 0.2 x 10~(-11) m~2 s~(-1) for polyHEMA at 37°C to lower values for the copolymers. The mass of water absorbed at equilibrium relative to the mass of dry polymer varied from 52-58 wt% for polyHEMA to lower values for the copolymers.