Thermodynamic Description of the γ' Phase in the Co-Al-W Based Superalloys

摘要

The phase equilibrium and the precipitation behavior of the γ' phase in the Co-Al-W-Ni-Cr superalloys were studied by thermodynamic method.The phase equilibrium of the Co-Al-W-15Ni-5Cr alloy at 900 °C was calculated,and it was found that there were a γ' single-phase region and a γ+γ' two-phase region.The effects of Al/W ratio on the precipitation of the γ' phase were studied,and it was clear that higher mole fraction of the γ' phase can be obtained with the Al/W ratio of 2.5.The stability of the γ' phase can be improved by adding of Ni,as well as the servicing temperature of the Co-Al-W based superalloys.The results obtained in this work can be used for the developing of the new-type Co-based superalloys.