Effects of Copper-Zinc Alloy Doped with Rare Earth Elements on Crystal of Calcium Carbonate

摘要

A copper-zinc alloy doped with rare earth elements was prepared and the mechanism was demonstrated in a simulating boiler and circulating cooling water with rigidity 1mmol·L<,-1>. The polar curve and scale inhibiting ability of the alloy was tested by a corrosion measurement system and a scale inhibition evaluation system, respectively. Scale samples were characterized with SEM and XRD. It is found that the transfer of cations could be promoted by doping with proper rare earth elements, and the corrosion potentials descend by 25~126mV. The results indicated that the copper-zinc alloy doped with rare earth elements has higher scale inhibiting ability of CaCO<,3>. The growth of calcite was affected by zinc ions dissolved because of primary battery reaction, and the transition of calcium carbonate from aragonite to calcite was hampered resulting in the proportion of aragonite to calcite is changed from 1.7∶1 to 2.7∶1.