IMPROVED PROCESS FOR MANUFACTURING SHEETS MADE OF ALUMINIUM-COPPER-LITHIUM ALLOY FOR AIRCRAFT FUSELAGE MANUFACTURE AND CORRESPONDING SHEET

摘要

The subject of the invention is a process for manufacturing a wrought product made of aluminum alloy comprising the following steps: a) casting a plate made of alloy comprising, in percentages by weight, Cu: 2.1 to 2.8; Li: 1.1 to 1.7; Mg: 0.2 to 0.9; Mn: 0.2 to 0.6; Ti: 0.01-0.2; Ag<0.1; Zr<0.08; Fe and Si #0.1 each; unavoidable impurities #0.05% each and 0.15% in total; remainder aluminum; b) homogenizing said plate at 480-520° C. for 5 to 60 hours; c) hot-rolling and optionally cold-rolling said homogenized plate to give a sheet; d) solution annealing the sheet at 470-520° C. for 5 minutes to 4 hours; e) quenching the solution-annealed sheet; f) controlled tensioning of the solution-annealed and quenched sheet with a permanent set of 1 to 6%; g) tempering of the tensioned sheet by heating at a temperature of at least 160° C. for a maximum time of 30 hours.