cold-formed or cold finished nickel - cobalt alloy with hoeg haallfasthet at foerhoejd temperature
cold-formed or cold finished nickel - cobalt alloy with hoeg haallfasthet at foerhoejd temperature
展开▼
机译:冷变形或冷成品镍钴合金,在费厄温度下具有霍格·哈尔法希特
展开▼
页面导航
摘要
著录项
相似文献
摘要
A work hardened nickel-cobalt alloy having high strength and ductility at temperatures of about 1300 DEG F is provided consisting essentially by weight of about 0.05% max carbon, about 20%-40% cobalt, about 6%-11% molybdenum, about 15%-23% chromium, about 1.0% max iron, about 0.0005%-0.020% boron, about 0%-4% titanium, about 0%-2% columbium and the balance nickel, the alloy having been cold worked at a temperature below the HCP-FCC phase transformation zone to a reduction in cross-section between 5% and 50%.