The preparation of superconducting epitaxial film using the method of liquid-phase epitaxial growth
The preparation of superconducting epitaxial film using the method of liquid-phase epitaxial growth
展开▼
机译:液相外延生长法制备超导外延膜
展开▼
页面导航
摘要
著录项
相似文献
摘要
Preparation of superconducting epitaxial film using the method of liquid phase epitaxial growth comprising the steps of:(1) melting the oxides of bismuth, calcium, strontium, and copper or the oxides of thallium, calcium, barium, and copper at temperature in the range of 900oC to 950oC to form a me(2) contacting the melt in (1) with magnesium oxide or mono crystalline materials;(3) lowering the temperature of the melt at a rate of 0.3-2oC/min until the temperature is within the range of 820oC to 890oC;(4) separating the melt and the magnesium oxide substrate or mono crystalline material to obtain a superconducting epitaxial film; and(5) quenching said film in (4) until the temperature thereof is at room temperature, whereby a superconducting epitaxial film having a thickness of 40 to 150 µm is obtained.
展开▼