The stainless steel wire null for the superfine belt which is superior in the drawability to below wire diameter
The stainless steel wire null for the superfine belt which is superior in the drawability to below wire diameter
展开▼
机译:超细皮带的不锈钢丝无效,可拉伸性优于丝径以下
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To obtain a stainless steel wire rod which is stably formed into a hyperfine stainless steel wire of =30mum diameter unlike a conventional wire rod by regulating the amounts of Al and O to specified very low values and the diameter of inclusions to a specified value. CONSTITUTION:The amounts of Al and O contained in a material for a Cr or Ni-Cr stainless steel wire rod are regulated to =0.006wt% Al and =10ppm O, and the diameter of inclusions is regulated to 10mum to obtain a stainless steel wire rod for a hyperfine wire. This wire rod can be drawn stably and continuously to =40mum, especially =30mum diameter without causing breaking. It is desirable that the amount of sol. Al is regulated to =0.005wt%. The amount of Al2O3 type inclusion with low plastic deformability can be reduced.
展开▼
机译:用途:通过将Al和O的含量调节到规定的极低值,并将夹杂物的直径调节到规定的值,从而获得一种能够稳定地制成直径小于等于30μm的超细不锈钢丝的不锈钢盘条值。组成:用于Cr或Ni-Cr不锈钢线材的材料中Al和O的含量被调节为<= 0.006wt%Al和<= 10ppm O,夹杂物的直径被调节为<10mum以得到用于超细钢丝的不锈钢线材。该线材可以稳定且连续地拉伸到<=40μm,特别是<=30μm的直径而不会引起断裂。理想的是溶胶的量。将Al调节至<= 0.005wt%。可以减少塑性变形性低的Al 2 O 3型夹杂物的量。
展开▼