Production mannered null mass of the high intensity stainless steel steel wire and the wire rod and the steel wire of the large diameter which is superior
Production mannered null mass of the high intensity stainless steel steel wire and the wire rod and the steel wire of the large diameter which is superior
展开▼
机译:高强度不锈钢钢丝以及优越的大直径的线材和钢丝的生产方式零质量
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To inexpensively provide thick-sized high strength stainless steel wire and wire rod having excellent ductility for inexpensively producing a product such as a thick-sized spring having excellent lightness and durability.;SOLUTION: The high strength stainless steel wire comprises, by mass, 0.01 to 0.13% C, 0.3 to 4.0% Si, 0.3 to 8.0% Mn, 1.0 to 6.0% Ni, 14.0 to 18.0% Cr and 0.05 to 0.20% N, has Md value of 50 to 120, has a tensile strength of 1,600 N/mm2, and has a wire diameter of ϕ4.5 to 15 mm: the Md value=551-462(C+N)-9.2Si-8.1Mn-29(Ni+Cu+Co)-13.7Cr-18.5Mo.;COPYRIGHT: (C)2008,JPO&INPIT
展开▼
机译:解决的问题:为了廉价地提供具有优良延展性的厚尺寸高强度不锈钢线和盘条,以廉价地生产诸如轻质和耐用性优异的厚尺寸弹簧之类的产品;解决方案:高强度不锈钢线包括按质量计,0.01至0.13%C,0.3至4.0%Si,0.3至8.0%Mn,1.0至6.0%Ni,14.0至18.0%Cr和0.05至0.20%N,Md值为50至120抗拉强度> 1,600 N / mm 2 Sup>,线径为4.5至15 mm:Md值= 551-462(C + N)-9.2Si-8.1Mn-29 (Ni + Cu + Co)-13.7Cr-18.5Mo。; COPYRIGHT:(C)2008,JPO&INPIT
展开▼