METAL FOIL FOR TAB TAPE HAVING HIGH YOUNG'S MODULUS AND HIGH YIELD STRENGTH AND ITS PRODUCTION
METAL FOIL FOR TAB TAPE HAVING HIGH YOUNG'S MODULUS AND HIGH YIELD STRENGTH AND ITS PRODUCTION
展开▼
机译:具有高杨氏模量和高屈服强度的胶带的金属箔及其生产
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To produce a metal foil excellent in lead deformation resisting- characteristic and heat resisting strength characteristic as a lead foil for TAB. ;CONSTITUTION: An alloy having a composition consisting of, by weight, 20-95% Cu, 0.3-11% Al, 0.05-3.0% Mn, 0.005-3.5% Ti, 0.5-10% Cr, 0.001-1.5% Mo, and the balance Fe with inevitable impurities is melted and cast, which is hot-rolled at 700-1000°C into a metal plate of 1.0-8mm plate thickness. This metal plate is subjected to primary cold rolling at 50-95% draft, to annealing at 800-1000°C, and then to secondary cold rolling at 1-70% draft. The resulting sheet is further subjected to solution heat treatment at 700-1000°C, to rapid cooling, and successively to aging treatment at 350-650°C. By this method, the metal foil wherein the aspect ratio of crystalline grain size and sheet thickness are regulated to ≤20 and ≤80μm, respectively, can be produced.;COPYRIGHT: (C)1994,JPO&Japio
展开▼