METALLIC FOIL FOR TAB TAPE HAVING HIGH YOUNG'S MODULUS AND HIGH YIELD STRENGTH AND ITS PRODUCTION
METALLIC FOIL FOR TAB TAPE HAVING HIGH YOUNG'S MODULUS AND HIGH YIELD STRENGTH AND ITS PRODUCTION
展开▼
机译:高杨氏模量和高屈服强度的卷带金属箔及其生产
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To produce a metallic foil having superior lead deformation resistance and heat resisting strength characteristics required of lead foil for TAB. ;CONSTITUTION: A molten metal having a composition consisting of, by weight, 20-95% Cu, 0.0005-1.0% Co, 0.005-3.5% Ti, 0.5-10% Cr, 0.001-1.5% Mo, and the balance Fe with inevitable impurities is cast into a metal plate of 0.5-8mm plate thickness at (100 to 50000)°C/sec solidification and cooling rate. This metal plate is subjected to primary cold rolling at 50-95% draft, to annealing at 800-1000°C, to secondary cold rolling at 5-70% draft, and successively to aging treatment at 350-650°C, by which the aspect ratio of crystalline grain size and sheet thickness are regulated to ≤20 and ≤80μm, respectively. By this method, the metallic foil minimal in anisotropy of characteristics, excellent in lead deformation resistance and heat resistance, and having high Young's modulus and high yield strength can be provided.;COPYRIGHT: (C)1994,JPO&Japio
展开▼