ALLOY ON THE BASIS OF VANADIUM CARBIDE SOLID SOLUTION IN NICKEL
ALLOY ON THE BASIS OF VANADIUM CARBIDE SOLID SOLUTION IN NICKEL
展开▼
机译:镍中碳化钒固溶体的合金
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: alloys. SUBSTANCE: alloy has, wt.-% vanadium carbide 1-3; solid solution of vanadium carbide in nickel at vanadium content 0.3-2.9% the rest. Alloy properties: microhardness is 2680-5050 MPa, corrosion stability (corrosion flow) is (2.9-3.7) (2,9-3,7)·10-5A/cm2. Alloy is used for fusing seat and cut-off fittings in manufacture of fluorine-containing compounds. EFFECT: enhanced quality of alloy. 1 tbl
展开▼
机译:领域:合金。物质:合金中有重量百分比为1-3的碳化钒;碳化钒在镍中的固溶体,其余的钒含量为0.3-2.9%。合金性能:显微硬度为2680-5050 MPa,腐蚀稳定性(腐蚀流量)为(2.9-3.7)(2,9-3,7)·10 -5 Sup> A / cm 2 < / Sup>。合金用于在制造含氟化合物中熔合阀座和切断件。效果:提高合金质量。 1汤匙