SURFACE PROTECTING FILM AND ACRYLIC RESIN PLATE SURFACE PROTECTED WITH THE SAME FILM
SURFACE PROTECTING FILM AND ACRYLIC RESIN PLATE SURFACE PROTECTED WITH THE SAME FILM
展开▼
机译:表面保护膜和用相同膜保护的丙烯酸树脂板表面
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To obtain the subject film useful for an acrylic resin plate for an optical product, having a tacky layer comprising an ethylene-vinyl acetate copolymer on one surface of a substrate layer composed of a high-density PE, and having a specific thickness ratio and excellent shearing properties, cutting properties and adhesiveness. ;CONSTITUTION: This film has (B) a tacky layer comprising an ethylene-vinyl acetate copolymer having 18-25wt.% vinyl acetate content on (A) one surface of a substrate layer composed of a high-density PE and the thickness ratio of the component A to the component B of 4/1 to 8/1. The component A has preferably 0.94-0.97g/cm3 density and the component B has preferably 2-15 melt flow rate. The whole thickness of this film is preferably 50-100μm. Lamination of an acrylic resin plate with the film is preferably carried out at 25-70°C of the resin plate temperature. The tack in the lamination is preferably 40-70gf/25mm when measured under conditions of 25mm width and 180° peel.;COPYRIGHT: (C)1996,JPO
展开▼
机译:用途:为了获得可用于光学产品的丙烯酸树脂板的主题薄膜,该薄膜在由高密度PE组成的基底层的一个表面上具有一个包含乙烯-乙酸乙烯酯共聚物的粘性层,并且具有特定的厚度比以及出色的剪切性能,切割性能和粘合性。 ;组成:该膜在(A)由高密度PE构成的基材层的一个表面上具有(B)粘性层,该粘性层包含具有18-25重量%乙酸乙烯酯含量的乙烯-乙酸乙烯酯共聚物。分量A到分量B为4/1到8/1。组分A优选具有0.94-0.97g / cm 3 Sup密度,组分B优选具有2-15的熔体流动速率。该膜的总厚度优选为50〜100μm。丙烯酸树脂板与膜的层压优选在树脂板温度的25-70℃下进行。当在25mm宽度和180°剥离的条件下测量时,层压中的粘性优选为40-70gf / 25mm .;版权:(C)1996,JPO
展开▼