SILICON STEEL SHEET EXCELLENT IN MAGNETIC PROPERTY AFTER ANNEALING BY SHORT-TIME HIGH FREQUENCY INDUCTION HEATING, AND ITS PRODUCTION
SILICON STEEL SHEET EXCELLENT IN MAGNETIC PROPERTY AFTER ANNEALING BY SHORT-TIME HIGH FREQUENCY INDUCTION HEATING, AND ITS PRODUCTION
展开▼
机译:短时高频感应加热退火后具有优异磁性的硅钢片及其生产
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To obtain an inexpensive nonoriented silicon steel sheet excellent in magnetic properties after magnetic annealing by short-time high frequency induction heating. ;SOLUTION: A steel, having a composition which consists of ≤0.005% C, 0.50-1.30% (Si+1/2Mn), ≤0.010% S, ≤0.002% Al, and the balance essentially Fe and in which inevitable contamination with Ti, Ni, V, and Zr is controlled so that (Ti+Nb+V+Zr)=0.001 to 0.01% is satisfied, is used. By this method, excellent iron loss can be obtained by means of magnetic annealing by short- time high frequency induction heating and an energy cost at the time of magnetic annealing can be reduced, and cost reduction of the nonoriented silicon steel sheet can be attained.;COPYRIGHT: (C)1998,JPO
展开▼
机译:解决的问题:通过短时间高频感应加热,获得在磁退火后的磁性能优异的廉价的无取向硅钢板。 ;解决方案:一种钢,其成分由≤0.005%C,0.50-1.30%(Si + 1 / 2Mn),≤0.010%S,≤0.002%Al组成,且其余部分基本上为Fe,并且不可避免地受到Fe的污染控制Ti,Ni,V和Zr,使得满足(Ti + Nb + V + Zr)= 0.001至0.01%。通过这种方法,可以通过短时高频感应加热的磁性退火获得优异的铁损,并且可以降低磁性退火时的能量成本,并且可以降低无取向硅钢板的成本。 ;版权:(C)1998,日本特许厅
展开▼