NONORIENTED SILICON STEEL SHEET HAVING EXCELLENT HIGH FREQUENCY MAGNETIC PROPERTY USED AFTER HEATING STAGE SUBSEQUENTLY TO FINISH ANNEALING AND PRODUCTION METHOD THEREFOR
NONORIENTED SILICON STEEL SHEET HAVING EXCELLENT HIGH FREQUENCY MAGNETIC PROPERTY USED AFTER HEATING STAGE SUBSEQUENTLY TO FINISH ANNEALING AND PRODUCTION METHOD THEREFOR
展开▼
机译:经过热处理和随后的生产方法后,具有优异的高频磁性能的规范化硅钢片
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a nonoriented silicon steel sheet which exhibits low core loss in high frequency, and is suitable as electric materials such as core materials used in high frequency.;SOLUTION: The nonoriented silicon steel sheet having excellent high frequency magnetic properties has a composition containing, by weight, ≤0.0015% C, 1.0 to 4.0% Si, 0.1 to 2.0% Al, 0.05 to 2.0% Mn, ≤0.1% (inclusive of zero) P, ≤0.005% (inclusive of zero) N, ≤0.02% (inclusive of zero) S and 0.4 to 5.0% Cr, and the balance substantially Fe.;COPYRIGHT: (C)2002,JPO