Laminating breathable waterproof fabric and its manufacturing method
Laminating breathable waterproof fabric and its manufacturing method
展开▼
机译:层压透气防水布及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a laminated moisture-permeable waterproof foam excellent in water pressure, moisture permeability, abrasion resistance, peel strength and elasticity and a manufacturing method thereof.;The present invention forms a reinforcing film layer by coating and drying a hydrophilic polyurethane resin composition to a thickness of 3 ~ 5㎛ on a release paper, water-in-oil dispersion (W / O) emulsion type polyurethane resin on the formed reinforcing film layer The composition is coated with a thickness of 15 to 25 μm and then dried in multiple stages to form a dry porous film layer. The formed film layer and the fabric is dot-bonded using a polyurethane adhesive and an embossing roll to prepare a laminated moisture-permeable waterproof fabric having a three-layer structure.;Laminating moisture-permeable waterproof foam of the present invention is a three-layer structure of the reinforcing film layer-dry porous film layer-fabric layer, the water pressure is 3.000 ~ 6.000 mm H 2 O, water vapor transmission rate is 11.000 ~ 14.00g / ㎡ 24hr, peel strength is 1.000 ~ 1.200g / ㎝, wear resistance has the property that the film layer is completely destroyed at the rotational speed of more than 4.500 when measuring KSK-0540.
展开▼
机译:本发明涉及具有优异的水压,透湿性,耐磨性,剥离强度和弹性的层压透湿防水泡沫体及其制造方法。本发明通过涂覆和干燥亲水性聚氨酯树脂形成增强膜层。在离型纸上使组合物的厚度为3〜5㎛,在形成的增强膜层上涂布油包水分散型(W / O)乳液型聚氨酯树脂。将组合物涂布15〜25μm的厚度,然后干燥。分多个阶段形成干燥的多孔膜层。使用聚氨酯粘合剂和压花辊将形成的膜层和织物点粘合,以制备具有三层结构的层压透湿防水织物。本发明的层压透湿防水泡沫是三层的。增强膜层-干燥多孔膜层-织物层的层结构,水压为3.000〜6.000 mm I> H 2 Sub> O,水蒸气透过率为11.000〜14.00 g /㎡24hr,剥离强度为1.000〜1.200g /㎝,耐磨性具有当测量KSK-0540时,在转速大于4.500时,膜层被完全破坏的特性。
展开▼