Karbonlanmis veya karbonla nitratlanmis bir çelik komponentin üretim prosesi ve bu komponentin yapilmasi için kullanilan çelik.
Karbonlanmis veya karbonla nitratlanmis bir çelik komponentin üretim prosesi ve bu komponentin yapilmasi için kullanilan çelik.
展开▼
机译:碳化或碳氮化钢构件的生产过程以及用于制造该构件的钢。
展开▼
页面导航
摘要
著录项
相似文献
摘要
A novel carburising or carbonitriding steel has the composition (by wt.) 0.2-0.26% C, 0.05-0.5% Si, 1 to less than 1.6% Mn, 0.4-1.5% Cr, 0.08 to less than 0.27% Mo, 0 to less than 0.6% Ni, 0.003-0.06% Al, 0-0.3% Cu, 0-0.1% S, less than 0.03% P, optionally up to 0.02% Te, up to 0.04% Se, up to 0.07% Pb and up to 0.005% Ca, balance Fe and impurities. Also claimed is a process for manufacturing a mechanical steel part by subjecting a rough steel part to surface carburising or carbonitriding, the steel having (a) the composition (by wt.) 0.15-0.35% C, 0-0.6% Si, 0 to less than 5% Mn + Cr + Ni + Mo, 0-0.1% Al, 0 to less than 0.5% Cu, 0-0.15% S, less than 0.03% P, optionally up to 0.02% Te, up to 0.04% Se, up to 0.07% Pb and up to 0.005% Ca, balance Fe and impurities; (b) a Jominy curve in which J3 = 45-50 HRC, J11 = 39-47 HRC and J25 = 31-40 HRC; and (c) average values J3m, J11m, J15m and J25m of five Jominy tests such that MOD(J11m - J3m x 13 divided by 22 - J25m x 8 divided by 22) = 2.5 HRC and J3m - J15m = 9 HRC.
展开▼
机译:一种新颖的渗碳或碳氮共渗钢具有以下组成(以重量计):0.2-0.26%C,0.05-0.5%Si,1至小于1.6%Mn,0.4-1.5%Cr,0.08至小于0.27%的Mo,0至0。小于0.6%的镍,0.003-0.06%的铝,0-0.3%的铜,0-0.1%的S,小于0.03%的P,可选地高达0.02%的Te,高达0.04%的Se,高达0.07%的Pb或更高到0.005%的钙,平衡铁和杂质。还要求保护一种通过在粗糙的钢零件上进行表面渗碳或碳氮共渗处理来制造机械钢零件的方法,该钢具有(a)组成(按重量计)0.15-0.35%C,0-0.6%Si,0至小于5%Mn + Cr + Ni + Mo,0-0.1%Al,0至小于0.5%Cu,0-0.15%S,小于0.03%P,可选地高达0.02%Te,高达0.04%Se ,最高0.07%的铅和最高0.005%的钙,其余的铁和杂质(b)Jominy曲线,其中J3 = 45-50 HRC,J11 = 39-47 HRC,J25 = 31-40 HRC; (c)五个Jominy测试的平均值J3m,J11m,J15m和J25m,以使MOD(J11m-J3m x 13除以22-J25m x 8除以22)= 2.5 HRC,而J3m-J15m = 9 HRC。
展开▼