A process for producing Bi-2223 high Tc superconductor in which fine MgO particles (0.1 &mgr;m) are homogeneously distributed to provide flux pinning centers in Bi-2223 high Tc superconductor in order to give enhanced critical current density under magnetic field, as compared to the Bi-2223 high Tc superconductor without MgO dispersion, when processed under similar conditions. The process comprises mixing partially converted Bi-2223 powder and MgO fine particles, drying to give mixed powder, filling in silver tube, drawing, rolling and heat-treating at a temperature and for a time sufficient to form Bi-2223 high Tc superconductor in which fine MgO particles are homogeneously distributed.
展开▼
机译:一种Bi-2223高T c Sub>超导体的制造方法,其中MgO细颗粒(<0.1&mgr; m)均匀分布,以在Bi-2223高T c 上提供磁通钉扎中心。与在没有类似MgO分散的Bi-2223高T c Sub>超导体相比,在相似的条件下进行处理时,为了在磁场下增强临界电流密度,Sub>超导体。该方法包括将部分转化的Bi-2223粉末和MgO细颗粒混合,干燥以得到混合粉末,填充到银管中,在一定温度和时间下拉伸,轧制和热处理足以形成Bi-2223高T c Sub>超导体,其中MgO细颗粒均匀分布。