Anti-reflection colored film-coated glass products prepared by forming on a transparent glass substrate with a refractive index of 1.47-1.53, a high refractive index film with a refractive index of 1.59-2.30 and a film thickness of 80-140 nm and containing 0-85% silicon oxides, 10-95% titanium oxides and 5-30% fine gold particles in terms of weight percentage, and by forming on the high refractive index film, a low refractive index film with a refractive index which is a value in the range of 1.35-1.58 and at least 0.20 smaller than the refractive index of the high refractive index film, having a film thickness of 70-99 nm and containing 90-100% silicon oxides in terms of weight percentage. These anti-reflection colored film-coated glass products of the invention have excellent anti-reflection performance for visible light and allow freedom in control of the color tones of transmitted light, and thus provide anti-reflection colored film-coated glass products with high visible light transmittance as well as the PDP optical filters that employ them.