PROBLEM TO BE SOLVED: To provide Li2O-Al2O3-SiO2-based transparent crystallized glass hardly causing crack even in being exposed in a combustion atmosphere for a long time and Li2O-Al2O3-SiO2-based crystalline glass used for producing the same.;SOLUTION: The Li2O-Al2O3-SiO2-based crystalline glass has ≥0.20/mm β-OH and ≤100 pieces /cm2 of crystals present on the surface and having ≥0.05 μm particle diameter and the Li2O-Al2O3-SiO2-based transparent crystallized glass is formed by heat-treating the Li2O-Al2O3-SiO2-based crystalline glass having ≥0.20/mm β-OH and ≤100 pieces/cm2 of crystals present on the surface and having ≥0.05 μm particle diameter.;COPYRIGHT: (C)2006,JPO&NCIPI