Rubber blend, useful for inner liner of vehicle tyres, comprises halo butyl rubber; additional rubber of e.g. butyl rubber or polybutadiene; delaminated talc; and carbon black
Rubber blend, useful for inner liner of vehicle tyres, comprises halo butyl rubber; additional rubber of e.g. butyl rubber or polybutadiene; delaminated talc; and carbon black
Rubber blend (A) for inner liner of vehicle tyres, comprises at least one halo butyl rubber (40-100) parts per weight (phr); at least one additional rubber (60 phr) of e.g. butyl rubber or polybutadiene; at least one delaminated talc (5-70 phr) with a BET-surface area of 10-40 m 2/g; and at least one carbon black (10-100 phr) with a cetyltrimethyl ammoniumbromide (CTAB) surface area of 10-25 m 2/g. Rubber blend (A), preferably for inner liner of vehicle tyres, comprises at least one halo butyl rubber (40-100) parts per weight (phr); at least one additional rubber (up to 60 phr) of butyl rubber, polybutadiene, styrene-butadiene copolymer, 3,4 polyisoprene, cis-1,4 polyisoprene, natural rubber, styrene-isoprene copolymer or styrene-isoprene-butadiene terpolymer; at least one delaminated talc (5-70 phr) with a BET-surface area of 10-40 m 2/g, according to DIN 66131, an average particle size (D 50) of 4-8 mu m (determined by means of a laser diffraction measurement) and a layer index (lamellarity index) of 3-15; and at least one carbon black (10-100 phr) with a cetyltrimethyl ammoniumbromide (CTAB) surface area of 10-25 m 2/g, according to ASTM D 3765 and a dibutylpthlate (DBP) number of 50-160 ml/100g, according to ASTM D 2414. An independent claim is included for a vehicle pneumatic tire with an inner liner based on (A).
展开▼
机译:用于车辆轮胎内衬的橡胶混合物(A),其每重量(phr)至少包含一种卤化丁基橡胶(40-100)份;至少一种其他橡胶(60 phr),例如丁基橡胶或聚丁二烯;至少一种BET表面积为10-40 m 2> / g的分层滑石(5-70 phr);至少一种炭黑(10-100 phr),十六烷基三甲基溴化铵(CTAB)的表面积为10-25 m 2> / g。橡胶共混物(A),优选用于车辆轮胎的内衬层,包含每重量(phr)至少一种卤化丁基橡胶(40-100)份;至少一种其他橡胶(最高60 phr),由丁基橡胶,聚丁二烯,苯乙烯-丁二烯共聚物,3,4聚异戊二烯,顺式1,4聚异戊二烯,天然橡胶,苯乙烯-异戊二烯共聚物或苯乙烯-异戊二烯-丁二烯三元共聚物组成;根据DIN 66131,至少一种BET表面积为10-40 m 2> / g的分层滑石(5-70 phr),平均粒径(D 50)为4-8μm(通过激光衍射测量值)和层指数(薄层指数)为3-15;至少一种炭黑(10-100 phr),根据ASTM D 3765,十六烷基三甲基溴化铵(CTAB)表面积为10-25 m 2> / g,邻苯二甲酸二丁酯(DBP)值为50-160 ml / 100g根据ASTM D2414。独立的权利要求包括基于(A)的具有内衬层的车辆充气轮胎。
展开▼