CONTINUOUSLY CAST SLAB FOR STEEL SHEET AND METHOD FOR PRODUCING THE SAME, AND STEEL SHEET AND METHOD FOR PRODUCING THE SAME
CONTINUOUSLY CAST SLAB FOR STEEL SHEET AND METHOD FOR PRODUCING THE SAME, AND STEEL SHEET AND METHOD FOR PRODUCING THE SAME
展开▼
机译:钢片连续铸造板及其制造方法,钢片及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a slab for steel sheet in which press cracking caused by large-sized inclusions is hard to occur, to provide a method for producing the same, a steel sheet, and a method for producing the same.;SOLUTION: The composition of inclusions in a continuously cast slab is controlled to the following, and then rolling is performed at a draft of ≥150: 80≤Ti oxide(%)+REM oxide(%)+Al2O3(%); CaO(%)≤5; 10≤Ti oxide(%); 15≤Al2O3(%)≤70; and 5≤REM oxide(%)≤0.31×Al2O3(%)+15. By this method, the steel sheet in which press cracking caused by large-sized nonmetallic inclusions upon press working is hard to occur can be obtained.;COPYRIGHT: (C)2007,JPO&INPIT
展开▼
机译:解决的问题:提供一种难以发生由大尺寸夹杂物引起的压裂的钢板用板坯,提供其制造方法,钢板及其制造方法。 :将连铸板坯中的夹杂物的组成控制为以下,然后以≤150的牵伸进行轧制:80%的Ti氧化物(%)+ REM氧化物(%)+ Al 2 Sub> O 3 Sub>(%);氧化钙(%)≤ 5; 10≤二氧化钛(%); 15≤ Al 2 Sub> O 3 Sub>(%)≤ 70;和5%REM氧化物(%)0.31倍Al 2 Sub> O 3 Sub>(%)+ 15。通过这种方法,可以得到在冲压加工时难以发生大型非金属夹杂物引起的冲压裂纹的钢板。版权所有:(C)2007,日本特许厅&INPIT
展开▼