SURFACE REFORMING METHOD FOR HARD COATING FILM, HARD COAT FILM OBTAINED THEREBY, OPTICAL FILM AND MANUFACTURING METHOD THEREOF
SURFACE REFORMING METHOD FOR HARD COATING FILM, HARD COAT FILM OBTAINED THEREBY, OPTICAL FILM AND MANUFACTURING METHOD THEREOF
展开▼
机译:硬涂膜的表面改质方法,由此获得的硬涂膜,光学膜及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a surface reforming method of harding coat film, capable of performing treatment in a short time by a process which is superior in environmental and safety respects and is more simplified and capable of improving the adhesiveness between a hard coat film and a functional film, while suppressing deterioration, even when applying a coating liquid comprising a composition that is different from the composition of the hard coating film and forming the functional film on the hard coating film formed on a base material film.;SOLUTION: In the surface reforming method of the hard coating film 12, the surface of the hard coating film 12 is treated by ultraviolet rays, wherein oxygen concentration in an ultraviolet irradiation environment is 3 to 10% and integrated light amount of ultraviolet rays, directly under an ultraviolet ray lamp, is 800 to 2,000 mJ/cm2.;COPYRIGHT: (C)2008,JPO&INPIT
展开▼
机译:解决的问题:提供一种硬化涂膜的表面改性方法,该方法能够在短时间内进行处理,该方法在环境和安全方面优异,并且被简化并且能够改善硬涂膜之间的粘附性。以及功能膜,即使在涂布包含与硬涂层膜的组成不同的组成的涂布液并在形成于基材膜上的硬涂层膜上形成功能膜的情况下,也抑制劣化。在硬涂膜12的表面改性方法中,通过紫外线对硬涂膜12的表面进行处理,其中,紫外线照射环境下的氧浓度为3〜10%,直接在紫外线下产生紫外线的累计光量。射线灯,800至2,000 mJ / cm 2 Sup> .;版权:(C)2008,JPO&INPIT
展开▼