COMPOSITION FOR CLASS thermal control coating 'solar reflectors'

摘要

1. A composition for thermal control coating grade "solar reflectors" liquid binder comprising potassium glass, metal oxide pigment and the solvent distilled water, characterized in that as binder a modified using liquid potassium glass, as a pigment a zinc-gallium oxide (ZnGaO1 + n where n = 0,0064). ! 2. A composition according to claim 1, characterized in that it comprises components in the following ratio, wt.%: modified liquid potassium glass 26,37-28,7 zinc-gallium oxide 42,28-45,23 28,40-28,97 distilled water! 3. A composition according to claim 1, characterized in that the modified liquid potassium glass is used with the module at a density of 3.3-3.8 g / cm 1,204-1,216. ! 4. A composition according to claim 1, characterized in that for modifying the liquid potash glass taken waterborne organic-based copolymer latex.