High crashworthiness Al-Si-Mg alloy and methods for producing automotive casting
High crashworthiness Al-Si-Mg alloy and methods for producing automotive casting
展开▼
机译:高耐撞性Al-Si-Mg合金及其生产汽车铸件的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention provides a casting having increased crashworthiness including an aluminum alloy of about 6.0 wt % to about 8.0 wt % Si; about 0.12 wt % to about 0.25 wt % Mg; less than or equal to about 0.35 wt % Cu; less than or equal to about 4.0 wt % Zn; less than or equal to about 0.6 wt % Mn; and less than or equal to about 0.15 wt % Fe, wherein the cast body is treated to a T5 or T6 temper and has a tensile strength ranging from 100 MPa to 180 MPa and has a critical fracture strain greater than 10%. The present invention further provides a method of forming a casting having increased crashworthiness.