CERIA-ZIRCONIA BASE COMPOSITE OXIDE, METHOD FOR PRODUCING THE SAME, AND CATALYST FOR PURIFICATION OF EXHAUST GAS USING THE CERIA-ZIRCONIA BASE COMPOSITE OXIDE

摘要

A ceria-zirconia base composite oxide contains a composite oxide of ceria and zirconia. In the ceria-zirconia base composite oxide, a content ratio between cerium and zirconium in the composite oxide is in a range from 43:57 to 48:52 in terms of molar ratio ([cerium]:[zirconium]). An intensity ratio of a diffraction line at 2θ=14.5° to a diffraction line at 2θ=29° {I(14/29) value} and an intensity ratio of a diffraction line at 2θ=28.5° to the diffraction line at 2θ=29° {I(28/29) value}, which are calculated from an X-ray diffraction pattern obtained by an X-ray diffraction measurement using CuKa after heating under a temperature condition of 1100°C in air for 5 hours, respectively satisfy the following conditions: I(14/29) value ≥ 0.015, and I(28/29) value ≤ 0.08.