SILICATE GLASS MATERIALS AND COLOR CONVERTER CONTAINING THEREOF AND WHITE LIGHT EMITTING DIODE
SILICATE GLASS MATERIALS AND COLOR CONVERTER CONTAINING THEREOF AND WHITE LIGHT EMITTING DIODE
展开▼
机译:包含其的硅酸盐玻璃材料和颜色转换器和白色发光二极管
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a silicate-based glass material capable of low-temperature firing, a color conversion member including the silicate-based glass material, and a white light emitting diode. The silicate-based glass material according to the present invention comprises (P 2 O 5 + B 2 O 3 ) -ZnO-SiO 2 based glass, wherein (P 2 O 5 + B 2 O 3 ) is 40 to 55 mol%, the ZnO is 25 to 40 mol%, the SiO 2 is 5 to 10 mol%, and the molar ratio of P 2 O 5 to B 2 O 3 is 8 to 10.
展开▼
机译:本发明涉及能够低温烧成的硅酸盐系玻璃材料,包括该硅酸盐系玻璃材料的颜色转换部件以及白色发光二极管。根据本发明的基于硅酸盐的玻璃材料包含(P 2 Sub> O 5 Sub> + B 2 Sub> O 3 Sub> )-ZnO-SiO 2 Sub>基玻璃,其中(P 2 Sub> O 5 Sub> + B 2 Sub> O 3 Sub>)为40至55 mol%,ZnO为25至40 mol%,SiO 2 Sub>为5至10 mol%,P 2 < / Sub> O 5 Sub>到B 2 Sub> O 3 Sub>是8到10。