An excellent product having excellent mechanical properties and having a fine structure can be produced not only for a thin product but also for a thick product without using a complicated process or apparatus. After the molten metal is poured into the lower mold of the press controlled so that the solid phase ratio becomes a desired constant value so that supercooling occurs, a semi-solid slurry is prepared, and at least the upper mold is the semi-solid A semi-solid casting forging method in which the semi-solid slurry is compressed to form a product by moving the upper die or the lower die at a speed of 0.1 to 1.5 m / s after contacting the slurry. is there. It is preferable to use crystal grains having a particle size that increases fluidity by compression, and the particle size is preferably 50 μm or less.
展开▼
机译:不仅对于薄的产品,而且对于厚的产品,都可以生产具有优异的机械性能并具有精细结构的优良产品,而无需使用复杂的工艺或设备。在将熔融金属倒入受控的压机的下模中以使固相比变为所需的恒定值以便发生过冷之后,制备半固态浆料,并且至少上模为半固态A半固态铸造锻造方法,其中半固态浆料在接触浆料后通过以0.1至1.5 m / s的速度移动上模或下模而被压缩以形成产品。在那儿。优选使用具有通过压缩而增加流动性的粒径的晶粒,并且粒径优选为50μm以下。
展开▼