Shear bands of as-cast and semi-solid Ti_(48)Zr_(27)Cu_(6)Nb_(5)Be_(14)bulk metallic glass matrix composites

摘要

The as-cast Ti_(48)Zr_(27)Cu_(6)Nb_(5)Be_(14)bulk metallic glass matrix composites(BMGMCs)were fabricated using a copper mold suction casting method.Then,the semi-solid BMGMC samples were obtained following an isothermal treatment(heating at 900°C for 10 min,then cooling with water).The microstructure and compression property were investigated by scanning electronic microscopy(SEM)and universal mechanical tester.As a result of the isothermal treatment,the crystal shapes change from fine,granular,and dendritic to spherical or vermicular,and the average crystal size of the as-cast and semi-solid samples is 2.2μm and 18.1μm,respectively.The plasticity increases from 5.31%in the as-cast to 10.23%in the semi-solid samples,with an increase of 92.66%.The shear bands from different areas of the side surfaces of as-cast and semisolid compression fracture samples were observed.The characteristic changes of multiplicity,bend,branch and intersection of shear bands in different areas indicate that the deformation of as-cast and semi-solid samples is non-uniform during compression.It is found that poor plasticity of the as-cast samples or good plasticity of the semi-solid samples are reflected by characteristics of the shear bands.The semi-solid isothermal treatment improves the plasticity by forming large crystals which can block the expansion of shear bands and promote the multiplicity of shear bands.