Thin monolayer polyethylene film with increased technical utility parameters and method for producing it
Thin monolayer polyethylene film with increased technical utility parameters and method for producing it
展开▼
机译:具有增加的技术实用性参数的单层聚乙烯薄膜及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
the application relates to thin jednowarstwowej polyethylene film of increased technical performance parameters, viz.,it contains: (a) 80 u00f7 87% high density polyethylene high density linear polyethylene with a flow within 0.2 u00f7 0.7 g / 10 min (iso 1133 - 190u00b0c / 2,16 kg) and density in the u00f7 0940 0960 g / cm3; (b) 10 - 15% linear low density polyethylene (lldpe) with a flow within 1.8 u00f7 2,2 g / 10 min (temp.190u00b0c / 2,16 kg method iso 1133) and density in the 0917 u00f7 0927 g / cm3); (c) 3 u00f7 5% polyethylene linear low density type heksenowego (mlldpe) with a flow within 0.8 u00f7 25 g / 10 min (iso 1133 - 190u00b0c / 2.16 kg) and density in the 0917 u00f7 0927 g / cm3. the subject application is also the way of film.
展开▼
机译:该申请涉及具有增加的技术性能参数的薄的聚乙烯薄膜,其包含:(a)80%的高密度聚乙烯,高密度线性聚乙烯,流动性在0.2≤0.7 g / 10分钟内(iso 1133-190公斤/2.16公斤)和密度,/ 9403 960克/立方厘米; (b)10-15%线性低密度聚乙烯(lldpe),其流量在1.8℃,2.2克/ 10分钟(190℃,/ 2.16千克方法iso 1133)之内,且密度在0917 u00f7 0927 g / cm3); (c)3 5%聚乙烯线性低密度型heksenowego(mlldpe),流量在0.8 u00f7 25 g // 10分钟(iso 1133-190 u00b0c / 2.16千克)以内,且密度在0917 u00f7 0927克/立方厘米。主题应用也是电影的方式。
展开▼