Highly elastic coefficient glass fiber composites and their glass fibers and composites
Highly elastic coefficient glass fiber composites and their glass fibers and composites
展开▼
机译:高弹性系数玻璃纤维复合材料及其玻璃纤维和复合材料
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention provides a high elastic modulus fiberglass composition and glass fibers and composites thereof. Among them, the content of each component of the glass fiber composition is in terms of weight percent, SiO 2 55-64%, Al 2 O 313-24%, Y 2 O 3 0.1-6 %, CaO 3.4-10.9%, MgO 8-14%, CaO + MgO + SrO 22%, Li 2 O + Na 2 O + K 2 O 2%, TiO 2 2%, Fe 2 O 3 1.5% and La 2 O 3 0-1.2%, and the ratio of the weight percentage is C1 = (Li 2 O + Na 2 O + K 2 O) / (Y 2 O 3 + La 2 O 3 ) is expressed as 0.26. This composition significantly improves the modulus of elasticity of the glass, effectively suppresses the crystallization tendency of the glass, decreases the liquidus temperature of the glass, and obtains a comparatively ideal ΔT value. In particular, Suitable.
展开▼
机译:本发明提供了高弹性模量的玻璃纤维组合物和玻璃纤维及其复合材料。其中,玻璃纤维组合物的各成分的含量以重量%,SiO 2 Sub> 55-64%,Al 2 Sub> O 3 13-24%,Y 2 O 3 0.1-6 Sub>%,CaO 3.4-10.9%,MgO 8-14%,CaO + MgO + SrO <22%,Li 2 O + Na 2 O + K 2 O <2%,TiO 2 Sub> <2%,Fe 2 Sub> O 3 Sub> <1.5%和La 2 < / Sub> O 3 Sub> 0-1.2%,重量比为C1 =(Li 2 Sub> O + Na 2 Sub> O + K 2 Sub> O)/(Y 2 Sub> O 3 Sub> + La 2 Sub> O 3 Sub> )表示为> 0.26。该组成显着提高了玻璃的弹性模量,有效地抑制了玻璃的结晶化趋势,降低了玻璃的液相线温度,并且获得了比较理想的ΔT值。特别适合。
展开▼