How radon barrier coating agent and a method for producing construction emitted by the cement

摘要

The invention1000 g tourmaline powder 1000 g sericite powder 1000 g water was mixed with 2000 g of water, and the mixture was transferred to a ball mill and ground by a ball mill for 24 hours to transfer the mineral filler solution to the filtration process, After filtration in a press process, the chylomorphic tourmaline sericite composition solution was transferred to a precipitation process and precipitated for 24 hours to prepare a porous mineral solution as a supernatant,Lead is extruded to a thickness of 1 mm to produce a lead having a diameter of 1 cm and a length of 20 cmA 1cm diameter and 20cm long silver bar was selected and then an oak barrel 2cm long and 20cm long oak bar was prepared and placed in a charcoal kiln and fired at 800C to produce a rodThe lead bar, the silver bar, and the bar bar were respectively connected to a 3-pole +-speed bar at the + electrode of the electrolysis apparatus, and the +-gap was fixed at 5 cm-10 cm.20 kg of the porous mineral solution and 200 g of oxygen chloride were mixed and charged into an electrolytic bath. The electrolytic bath was fixed at 3 volts and 13 amps, and electrolysis was carried out while the lead, silver, Silver nanoparticles, silver and white carbon porous mineral solutions were prepared, and then 1000 g of the powdery brown powder, 2000 g of the nano-lead, silver, and carbon porous mineral solution prepared above, and 200 g of the water-soluble urethane coating agent were mixed and put in a ball-After 10 hours of pulverization to prepare a soft white coating composition,20 cm 2 of 1 cm diameter silver (Ag) was prepared and connected to the positive electrode of the electrolyzer. Then, 20 kg of water and 100 g of 0.1 N hydrochloric acid were mixed in the electrolytic cell, and the positive electrode was placed in the electrolytic cell. After the current was fixed at 3 amps and 13 amps, the positive electrode was completely dissolved in the water of the electrolytic cell, and 5000 g of water was mixed with 100 g of the silver nano solution to prepare silver nano-ionized water. Then, 1000 g of chrysanthemum powder, 500 g of tourmaline powder, 1000 g of the sericite powder was mixed,And 1000 g of the mixed powder, 200 g of the water-soluble urethane coating agent, and 2000 g of the silver ion water are milled for 10 hours by a ball mill. The present invention relates to a method for manufacturing a radon blocking agent released from cement and a construction method thereof.