MAGNESIUM-CONTAINING, ALUMINUM-BASED ALLOY FOR THIN-WALL CASTINGS

摘要

An aluminum-magnesium alloy is disclosed which provides superior properties for casting in steel dies and good ductility for forming castings of complex shapes, including thin-wall portions. The aluminum-based alloy contains, in weight percent, about 2-15 percent magnesium, 0.2 to 3 percent silicon, 0.05 to 0.5 percent chromium, 0.05 to 0.5 percent manganese, 0.05 to 0.2% titanium, and a minimal content of iron. In its molten state this aluminum-magnesium-chromium alloy can be pushed into the molding cavities of iron-based dies in a high pressure die casting procedure and conform to complexly-shaped die surfaces with thin cavity portions without dissolving appreciable amounts of iron or experiencing die soldering on the die surfaces. The resulting castings display good strength and ductility and can be further enhanced by an artificial aging process after solution heat treatment.