Electroplating bath for forming a porous straight tubular iron group element plating film and a method for forming a porous straight tubular iron group element plating film using this electroplating bath
Electroplating bath for forming a porous straight tubular iron group element plating film and a method for forming a porous straight tubular iron group element plating film using this electroplating bath
展开▼
机译:形成多孔性直管状铁族元素镀膜的电镀浴和使用该电镀浴形成多孔性直管状铁族元素镀膜的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a technology capable of increasing a specific surface area of an iron group element plating film.SOLUTION: There are provided an electroplating bath for forming a porous cylindrical iron group element plating film by containing tertiary amine represented by the following formula (I), where Rrepresents a linear or branched alkyl group having 1 to 6 carbon atoms, Rrepresents a linear or branched alkyl group having 1 to 6 carbon atoms or an aryl which may have a substituent, Rrepresents an aryl group which may have a substituent into an iron group element plating bath, a method for forming the porous cylindrical iron group element plating film by electroplating at 0.5 to 4 A/dmfor 10 min. or more using the same and the porous cylindrical iron group element plating film obtained thereby.SELECTED DRAWING: Figure 2
展开▼
机译:解决的问题:提供一种能够增加铁族元素镀膜的比表面积的技术。解决方案:提供一种电镀浴,其通过包含以下所示的叔胺来形成多孔的圆柱形铁族元素镀膜。式(I),其中R代表具有1至6个碳原子的直链或支链烷基,R代表具有1至6个碳原子的直链或支链烷基或可以具有取代基的芳基,R代表可以具有一个碳原子的芳基。取代基形成铁族元素镀浴的方法,该方法是通过以0.5至4 A / dm的电流电镀10分钟来形成多孔圆柱形铁族元素镀膜。相同或更大的尺寸以及由此获得的多孔圆柱形铁族元素镀膜。选图:图2