Stress Dependence of Ultrasonic Velocity in Unidirectional Graphite/Epoxy Composites for Longitudinal Waves Propagating Along the Direction of Stress

摘要

The first measurements of the stress induced velocity changes for propagation directions along the direction of applied stress in gr/ep composites have been presented. For propagation and stress direction perpendicular to the fiber direction, the data demonstrated a linear relation between normalized velocity shift and stress. After corrections for the delay line were made, the slope or SAC was determined and compared favorably with the expected value calculated from the previously determined nonlinear coefficients of this material. The ratio of the SAC to the elastic compliance for this direction of loading was evaluated and found to have a value similar to numerous other materials which have very different linear elastic properties. Measurements with stress and propagation along the fibers yielded unusual behavior. The curves were very nonlinear and even shifted direction at higher loads. The large scatter in the data due to bond variations made separation of material effects from bond induced artifacts impossible. Thus the SAC, R, and the remaining two unknown TOEC's could not be determined for this direction of propagation. These measurements further expand the basis of determining nonlinear elastic properties of composite materials. These properties may be useful in developing much needed NDE techniques to determine such important parameters as residual stress after cure and residual strength after impact damage. Additional study is needed to measure the nonlinear behavior in other composite materials including angle ply laminates. Also, other techniques to measure elastic nonlinearity such as harmonic generation should be applied to composites to improve the understanding of these properties and their importance.