Crystal growth of compound semiconductors in a low-gravity environment (InGaAs crystals) (M-22)

摘要

Compound semiconductor crystals, such as gallium arsenide and indium phosphide crystals, have many interesting properties that silicon crystals lack, and they are expected to be used as materials for optic and/or electro-optic integrated devices. Generally speaking, alloy semiconductors, which consist of more than three elements, demonstrate new functions. For example, values of important parameters, such as lattice constant and emission wavelength, can be chosen independently. However, as it is easy for macroscopic and/or microscopic fluctuations of composition to occur in alloy semiconductor crystals, it is difficult to obtain crystals having homogeneous properties. Macroscopic change of composition in a crystal is caused by the segregation phenomenon. This phenomenon is due to a continuous change in the concentration of constituent elements at the solid-liquid interfacing during solidification. On Earth, attempts were made to obtain a crystal with homogeneous composition by maintaining a constant melt composition near the solid-liquid interface, through suppression of the convection flow of the melt by applying a magnetic field. However, the attempt was not completely successful. Convective flow does not occur in microgravity because the gravity in space is from four to six orders of magnitude less than that on Earth. In such a case, mass transfer in the melt is dominated by the diffusion phenomenon. So, if crystal growth is carried out at a rate that is higher than the rate of mass transfer due to this phenomenon, it is expected that crystals having a homogeneous composition will be obtained. In addition, it is also possible that microscopic composition fluctuations (striation) may disappear because microscopic fluctuations diminish in the absence of convection. We are going to grow a bulk-indium gallium arsenide (InGaAs) crystal using the gradient heating furnace (GHF) in the first material processing test (FMPT). The structure of the sample is shown where InGaAs polycrystals in a crucible are doubly sealed in two quartz tubes for safety. The GHF consists of two zones, namely, high temperature and low temperature zones, which results in a large temperature gradient at the interface. Crystal growth is performed by moving the furnace (i.e. the temperature profile) from the left to right at a definite rate. Thus, we will grow crystals both on Earth and in space under the same conditions. As previously described, it is possible to obtain good quality crystals which are homogeneous in composition both macroscopically and microscopically due to the lack of convection in space. We are planning to study the effects of convection on crystal growth from a melt by comparing and characterizing the properties of crystals grown on Earth with those grown in space.