Burn rates of TiH2/KClO4/Viton and output testing of NASA SKD26100098-301 pressure cartridges

摘要

The burn rates of the pyrotechnic TiH2/KClO4/Viton with a mass ratio of 30/65/5 have been measured as a function of pressure in nitrogen up to 312 MPa(45 Kpsi). The burn rates were fit to R = a pn, with a = 2.055 cm/sec/MPan and n = 0.472 between 0.15 MPa (22 psi) and 21.6 MPa (3.13 Kpsi) and a = 4.38 cm/sec/MPan and n = 0.266 between 70 MPa (10.15 Kpsi) and 312 MPa (45.25 Kpsi). The decrease in slope at the higher pressures is attributed to a diffusion limited reaction. No acoustically driven flame instabilities or large conductive-to-convective burn transitions were observed. Solid reaction products were analyzed by x-ray diffraction and scanning electron microscopy (SEM). X-ray diffraction detected only TiO2 and KC1. SEM showed that the particle size of the reaction products increased as the nitrogen pressure increased. There were no anomalous characteristics of the burn of this pyrotechnic that could be interpreted as a cause of the o-ring blow-by problem in the forward shear bolt assembly. Three NASA SKD26100098-301 pressure cartridges were fired into a fixed volume vessel that was sealed with an O-ring. A maximum pressure of 181.7 MPa(26,350 psi) was reached in around 100 ,mu sec for two shots fired into a volume of 16.3 cm3(0.996 in3). A maximum pressure of 33,460 psi was reached for one shot fired into a volume of 9.55 cm3(0.583 in3). The O-ring burned through on one shot in the larger volume and leaked on the other two thereby simulating the effects of an O-ring leak. The results imply that the piston in the shear bolt assembly would receive a large impulse even if there was a leak in an O-ring seal.