A Comparison of the Mechanical Properties and Microstructures of Intermetallic Matrix Composites Fabricated by Two Different Methods

摘要

The tensile properties of SCS-6 SiC fiber-reinforced Ti-24Al-11Nb (at. pct) have been measured over the past several years by a number of investigators. These composites have been fabricated by different techniques and tend to exhibit a large amount of scatter in the longitudinal tensile properties. To date, it is not known if one optimized fabrication method provides composites with improved mechanical properties over those produced by other optimized methods, since carefully controlled experiments have not been performed to determine this. Thus, the purpose of the present study was to compare the longitudinal tensile strengths of SCS-6 SiC/Ti-24Al-11Nb composites that had been fabricated by the powder-cloth method and the low pressure plasma spray (LPPS) method. In this study, the same lots of matrix powder and reinforcing fiber were used for fabricating the composites. It was determined that the powder-cloth and plasma spray methods produced composites having very similar tensile properties. Both fabrication methods induced damage in a small percentage of fibers, which manifested itself in the form of bimodal Weibull distributions of extracted fiber strengths. It appeared that the particular lot of SCS-6 fiber used in fabricating both types of composites was more susceptible to fabrication damage than those used in previous studies. This article also shows the dramatic effect that different handling and testing techniques can have on measured fiber strengths.