Effects of Tensile Preloads on the Impact Response of Carbon/Epoxy Laminates

摘要

The effects of tensile preloads on the tension-after-impact (TAI) strength ofcomposite laminates of IM7/8551-7 were examined. A failure threshold curve was first determined so the most informative values for preload/impact energy combinations could be determined. The impact tests were instrumented so maximum load of impact, as well as several other parameters could be measured. The elastic response data indicate that as the tensile preload is increased, the maximum load of impact also increases. The damage data show that at low impact energies, the damage/failure is an 'all-or-nothing' event but at higher impact energies, a region of preload values exists where the coupons could sustain damage, yet not fail catastrophically.