Experimental Investigation of Effects of Random Loading on the Fatigue Life of Notched Cantilever-Beam Specimens of 7075-T6 Aluminum Alloy

摘要

Results of random-loading fatigue tests on 125 notched cantilever-beam specimens and constant-amplitude fatigue tests on 46 similar specimens are presented in terms of the root-mean-square value of peak stresses. The results from the two sets of tests are compared on the basis of time to failure, where the results from the constant-amplitude tests are expressed in terms of an equivalent time to failure based on the natural period of vibration. Compared on this basis, failure at the lower stress levels occurred in a shorter time for the random loading than for the constant-amplitude loading, whereas at the higher stress levels failure occurred in the reverse order. A theoretical result for random loading is also presented and compared with the experimental results. The theoretical result shows good agreement with experiment for low values of stress but underestimates the time to failure at the higher stresses.