Microstructure and Mechanics of Superconductor Epitaxy via the Chemical Solution Deposition Method. Report for September 1, 2003 to December 31, 2006.

摘要

Initially the funds were sufficient funds were awarded to support one graduate student and one post-doc. Lange, though other funds, also supported a graduate intern from ETH Zurich, Switzerland for a period of 6 months. The initial direction was to study the chemical solution deposition method to understand the microstructural and mechanical phenomena that currently limit the production of thick film, reliable superconductor wires. The study was focused on producing thicker buffer layer(s) on Ni-alloy substrates produced by the RABiTS method. It focused on the development of the microstructure during epitaxy, and the mechanical phenomena that produce cracks during dip-coating, pyrolysis (decomposition of precursors during heating), crystallization and epitaxy. The initial direction of producing thicker layers of a know buffer layer material was redirected by co-workers at ORNL, in an attempt to epitaxially synthesize a potential buffer layer material, LaMnO3, via the solution route. After a more than a period of 6 months that showed that the LaMnO3 reacted with the Ni-W substrate at temperatures that could produce epitaxy, reviewers at the annual program review strongly recommended that the research was not yielding positive results. The only positive result presented at the meeting was that much thicker films could be produce by incorporating a polymer into the precursor that appeared to increase the precursors resistance to crack growth. Thus, to continue the program, the objectives were changed to find compositions with the perovskite structure that would be chemically compatible with either the Ni-W RABiTS or the MgO IBAD Ni-alloy substrates, and produce a better lattice parameter fit between either of the two substrates. At the start of the second year, the funding was reduced to 2/3s of the first year level, which required the termination of the post-doc after approximately 5 months into the second year. From then on, further funding was intermittent to say the least, and funding to support the student and the research expenses has to be supplemented by Langes gift funds. During the first part of the second year, strontium zirconate was identified as an alternative to lanthanum manganite as a buffer layer for use on the IBAD MgO superconducting wire. A lattice parameter of 4.101 Angstroms offers a reduced lattice mismatch between the MgO and SrZrO3. Studies were focused on investigating hybrid precursor routes, combining Sr acetate with a number of different Zr alkoxides.